Two-part room temperature vulcanizable systems

ABSTRACT

There is provided by the present invention a two-part room temperature vulcanizable silicone rubber composition which is exceptionally stable to reversion and specifically to reversion of the cured composition caused by water comprising a silanolstopped diorganopolysiloxane, filler, an alkyl silicate and a catalyst where the catalyst is a reaction product of an organic tin oxide compound with the hydrocarbon ester of an oxygencontaining acid having at least one oxygen atom in the acid radical attached to a replaceable acid hydrogen atom. The hydrocarbon ester can be either an inorganic acid or a carboxylic acid. The preferred catalyst in the present invention is the reaction product of dibutyl tin oxide and a phthalate ester.

United States Patent [191 Hamilton, Jr. et al.

[ 1 Oct. 1, 1974 TWO-PART ROOM TEMPERATURE VULCANIZABLE SYSTEMS {75] Inventors: Stephen B. Hamilton, Jr.,

Schenectady; Warren R. Lampe, Ballston Lake, both of NY.

[73] Assignee: General Electric Company,

Waterford, NY.

[22] Filed: Aug. 9, 1973 [21] Appl. No.: 387,460

[52] US. CL... 260/18 S, 117/132 BS, 117/1395 R, 117/143 A, 260/33.6 SB, 260/37 SB, 260/46.5 G, 260/825 [51] Int. Cl. C08f 19/14 [58] Field of Search 260/46.5 G, 18 S, 37 SB, 260/825, 33.6 SB

[56] References Cited UNITED STATES PATENTS 2,597,920 5/1952' Carroll 260/45.75 K 3,070,566 12/1962 Nitzsche et a1. 260/46.5 G

8/1970 Gibbon et al. 260/825 5/1972 Leebrick 260/46.5 G

[5 7] ABSTRACT There is provided by the present invention a two-part room temperature vulcanizable silicone rubber composition which is exceptionally stable to reversion and specifically to reversion of the cured composition caused by water comprising a silanol-stopped diorganopolysiloxane, filler, an alkyl silicate and a catalyst where the catalyst is a reaction product of an organic tin oxide compound with the hydrocarbon ester of an oxygen-containing acid having at least one oxygen atom in the acid radical attached to a replaceable acid hydrogen atom. The hydrocarbon ester can be either an inorganic acid or a carboxylic acid. The preferred catalyst in the present invention is the reaction product of dibutyl tin oxide and a phthalate ester.

40 Claims, No Drawings TWO-PART ROOM TEMPERATURE VULCANIZABLE SYSTEMS BACKGROUND OF THE INVENTION Two-part room temperature vulcanizable rubber compositions are well known compositions in the prior art. Such compositions generally comprise an ingredients a silanol-stopped diorganopolysiloxane and a filler which comprises one-part of the two-component composition. The second part of the two-component composition usually comprises an alkyl silicate or a partial hydrolysis product of an alkyl silicate as the crosslinking agent combined with a catalyst which traditionally has been the metallic salt of an organic monocarboxylic or dicarboxylic acid in which the metal ion is selected from the class consisting of lead, tin, zirconium, antimony, iron, cadmium, barium, calcium, titanium, bismuth and manganese.

One trouble with this type of catalyst which has been experienced in practice is that the catalyst is not adequately soluble and in most cases is found to be insoluble in the alkyl silicate of the second component. As a result when the two components are mixed together to cure the composition to form a cured two-part room temperature vulcanizable silicone rubber composition,

it is found the insoluble catalyst does not readily disperse throughout the entire composition and is onlly erratically dispersed through the total composition. As a result of the inadequate dispersion, the two-part room temperature vulcanizable silicone rubber composition does not cure uniformly. In fact, there may be experienced weak spots in the cure even after the two-part room temperature vulcanizable silicone rubbercomposition has been allowed to lie for a substantial period of time so as to allowit to cure. The solution to this problem has been met by, in most cases, urging the applicators of the two-part RTV system (RTV standing for room temperature vulcanizable silicone rubber composition) to mix the two components one into the other very thoroughly. However, as can be envisioned, this is not only time consuming but extremely difficult to carry out in practice.

Another problem with the utilization of the metal salts of a monocarboxylic acid or dicarboxylic acid catalyst is'that after the two-part RTV system is cured and especially in warm and humid climates. water vapor or moisture might react with the catalyst which was present in the cured two-part RTV system and result in the liberation of acids which over a period of time will degrade the cured two-part RTV system to some extent. Although the two-part RTV system even if degraded in this manner, will retain most of its physical properties, nevertheless, there resulted the phenomenon of what is known as chalking, that is, the surface RTV layer would degradesomewhat and present an unsightly appearance to the eye. This reversion or degradation of the RTV system was.especially found to be evidentwhen the traditional two-part RTV/systems were cared to form roof coatings in humid climates.

Accordingly, it would be'highly desirable to provide a catalyst system for a two-part RTV system which catalyst would be easily soluble in the alkyl silicate crosslinking agent in traditional two-part RT V systems as well as the linear silanol-stopped diorganopolysiloxane material and also to provide a catalyst which even in hot and humid climates would not release or degrade It is an additional object of the present invention to provide .a catalyst for a two-part RTV system which catalyst even in hot and humid climates will not release any acids which might degrade the cured RTV polymer.

It is an additional object of the present invention to provide a novel catalyst for two-part RTV systems which can easily be incorporated into a two-part selfbonding RTV system so as to produce from such twopart RTV systems coatings and films of exceptional hydrolytic stability.

These and other objects of the present invention are accomplished in accordance with the disclosure set forth herein below.

. SUMMARY OF THE INVENTION In accordance with the above objects, there is provided by the presentinvention a two-part room' temperature vulcanizable silicone rubber composition with improved hydrolytic resistance and stability comprising (a) a linear fluid organopolysiloxane containing terminal silicon bonded hydroxy groups and having a viscosity of 500 radicals to 10,000,000 centipoise when measured at 25C, the organic groups of the aforesaid organopolysiloxane representing monovalent hydrocarbon radicals, (b) a filler, (c) from 0.1 to 15 percent by weight of an alkyl silicate selected from the class consisting'of l) a monomeric organosilicate corresponding 0, the general formula,

where R is a radical selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and R is selected from the class consisting of alkyl, haloalkyl, aryl, haloaryl, alkenyl, cycloalkyl, cycloalkenyl, cyanoalkyl, alkoxy and acyloxy radicals and (2) a liquid partial hydrolysis product of the aforementioned organosilicate monomeric compounds. The alkyl silicate or the partial hydrolysis product of the alkyl silicate is a cross-linking agent which is kept separate from the linear silanolstopped diorganopolysiloxane and the tiller. Normally, the filler is incorporated into the silanol-stopped diorganopolysiloxane polymer to form component (A) of the two-part system and component (B) comprises the alkyl silicate cross-linking agent or the partial hydrolysis product of this material.

Into component (B) and more specifically mixed in with component (B) there is provided by the present invention the incorporation of a novel catalyst which is a reaction product of anorgano tin oxide having the formula RIIRIIISnO where R" and R' are monovalent hydrocarbon radicals; with a hydrocarbon ester of an oxygen containing acid having at least one oxygen atom in the radical attached to a replaceable acid hydrogen atom. Preferably, there is incorporated into the composition, 0.1 to 5 percent by weight of the linear silanol-terminated organopolysiloxane of this novel catalyst.

As is well known, other ingredients may be mixed into either component (A) or component (B) of the two-part RTV system which agents are normal constituents of two-part RTV systems. The preferred novel catalyst of the present case is the reaction product of dibutyl tin oxide with a phthalate ester. Generally, R and R may be selected from any. hydrocarbon radicals but more preferably are selected from alkyl and aryl radicals such as methyl, ethyl or phenyl of up to 12 carbon atoms. The tin oxide is reacted with a hydrocarbon ester of either an inorganic acid or monocarboxylic' acid or dicarboxylic acid.

It is desired to produce a self-bonding two-part RTV system having the novel catalyst set forth above, then there may be incorporated into the composition and preferably in component (B) of the composition a selfbonding agent comprising 0.1 to 10 percent by weight of the diorganopolysiloxane of a nitrogenfunctional silane of the formula l Era-08w residue functionalized by a member selected from the class consisting of amino, cyano, 0x0 and ester, a is a whole number that varies from O to 2 in the foregoing fumula.

There is also provided by the present invention a process for producing a two-part RTV system and more particularly a novel process for producing a two-part RTV where there is incorporated in the mixing of the two-part RTV system in place of the traditional metal.

salt of a carboxylic acid catalyst, the novel catalyst of the present case as set forth above.

In addition, there is provided by the present invention a process for producing a two-part RTV system which is exceptionally hydrolytically stable as well as' one that will self-bond to various surfaces such as metal, wood and masonry surfaces by the use in the process for forming the two-part RTV system in addition to the novel catalyst of the present case, a nitrogen functional silane as set forth in formula (1) above.

DESCRIPTION OF THE PREFERRED EMBODIMENT Asstated previ'ously, the organo tin oxides which are utilized inthe present invention to form-the reaction productcatalyst preferably have the formula,

where R" and R' are monovalent hydrocarbon groups selected from the class consisting of alkyl radicals such as methyl, ethyl, propyl, butyl,- etc.; mononuclear and binuclear aryl radicals such as phenyl, naphthyl and etc.; aralkyl radicals such as phenylmethyl and etc. Even more preferably the R and R radicals are selected from alkyl, lower alkyl radicals and mononuclear aryl radicals such as methyl, ethyl and phenyl of up to 8 carbon atoms.

Among the organo tin oxides which are preferred to form the catalyst of the present case are dimethyl tin oxide, diamyltin oxide, didecyl tin oxide, dilauryl tin oxide, dipropenyl tin oxide, diphenyl tin oxide, ditolyl.

tin oxide, methylethyl tin oxide and phenylbutyl tin oxide.

In the claim language in defining the catalyst of the present case, aswell as in the specification, the term oxygen-containing acid having at least one oxygen atom in an acid radical attached to a replaceable acid hydrogen atom is used to define organic acids commonly referred to as monocarboxylic acids and dicarboxylic acids and inorganic acids containing at least one oxygen atom in the acid radical attached to a replaceable acid hydrogen atom such as phosphorous acid, phosphoric acid, silicic acid, sulfurous acid, sulfuric acid, arsenious acid arsenic acid, boric acid, perchloric acid, chlorous acid, periodic acid, isdous acid, iodic acid, chromic acid, hypochloric acid, nitrous acid, nitric acid, selenic acid, selenous acid, tellurous acid, telluric acid, titanic acid, bromous acid, and the like.

The organic tin oxide may be reacted with any hydrocarbon ester which may be either a saturated hydrocarbon ester or an unsaturated hydrocarbon ester. Among the esters of an oxygen-containing acid which is reacted with the tin oxide to produce the desired reaction product catalyst are hydrocarbon esters such as ethyl ortlio silicate, triethyl arsenate, n-propyl silicate, di-npropyl sulfate, tributyl phosphate, n-octyl nitrate, di-ndodecyl sulfate, tri-o-cresyl phosphate, tri-p-cresyl phosphate, amyl borate, methyl acetate, diemthyl maleate, dimethyl phthalate, ethyl benzoate, diethyl maleate, diethyl phthalate,'diethyl m-phthalate, diethyl p-.

phthalate, butyl butyrate, dibutyl sebacate, dioctyl phthalate, butyl glycolphthalate, n-butyl propionate, ethylene butyrate, ethylene laurate, 2-propenyl butanoate, phenol. acetate, phenyl laurate, diphenyl phthalate, phenyl salicylate, B-naphthyl benzoate, and 2-napthyl lactate. Even more preferred hydrocarbon esters which may be utilized in the present invention to produce the desired catalysts are as follows: methyl acetate, ethyl acetate, n-propyl acetate, isopropyl acetate, butyl acetate, phenol acetate, M-cresyl acetate, methyl propionate, n-butyl propionate, sec-butyl propionate, ethylene propionate, ethyl butyrate, n-propyl butyrate, ethylene butyrate, 2-propenyl butanoate, pentyl butanoate, dimethyl maleate, diethyl maleate, ethyl benzoate, amyl benzoate, B-naphthyl benzoate, dimethyl phthalate, diethyl phthalate, diethyl m-phthalate, diethyl-pphthalate, butyl glycol phthalate, diphenylphthalate, dibutyl sebacate, ethylene stearate, ethylene laurate, phenyl'laurate,phenyl salicylate, 2-naphthyl lactate. Even more preferred hydrocarbon esters of monocarboxylic acids and dicarboxylic acids are the following hydrocarbon esters for use as reactants with the tin oxides described above for producing the desired catalyst of the present case: dimethyl maleate, dimethyl phthalate, monoethyl maleate, monoethyl phthalate, diethyl maleate, diethyl phthalate, dipropyl maleate, dipropyl phthalate, dibutyl maleate, dibutyl phthalate, dialauryl maleate, dilauryl phthalate.

To obtain the reaction productof the present case for use in a two-part RTV system of the present case, the reaction is quite simple which comprises mixing the organo tin oxide and the ester together in an agitator and heating the mixture while it has been continuously-agitated during a period of about 1 hour or more. During the initial stage of heating, the mixture tends to solidify and form a stiff viscous mass which as the reaction progresses changes into a liquid state as more of the catalyst reaction product is formed. When the reaction is completed, a substantially clearliquid is obtained.

The organo tin oxide and hydrocarbon ester are preferably reacted in equal molar quantities although a molar quantity of the ester may be reacted with several moles of the organo tin oxide, for example, one mole of diethyl phthalate or ethyl orthosilicate can be reacted with l,2 or 4 moles of organo tin oxide. in addition, one mole of tri-cresyl phosphate can be reacted with as many as 6'moles of the organo tin oxide. The reaction may be carried out at various temperatures anywhere from room temperature up to above 250C. Preferably, a temperature of from 100 to 225C is desired because the reaction is completed in the specified time period of 1 hour at this temperature range. In addition, for any particular mixture of an ester of an oxygen-containing acid as defined above and an organo tin oxide as defined above, the satisfactory reaction temperature range is the temperature at which the mixture sets up to form a stiff viscous mass. In addition, it may be desired to increase the temperature at 5 above this temperature in order to have the reaction proceed more rapidly. As can be envisioned, the higher the temperature is within the above preferred range of 100 to 225C, the faster the reaction will proceed to produce the desired reaction product. For example, when an equal molar mixture of a diethyl phthalate and dibutyl tin oxide is agitated and heated to a temperature of 150C, the slurry formed to a stiff viscous mass which if maintained at this temperature chemically reacts to form a clear-like yellow reaction product, the reaction being completed after a reaction period of about 1 hour as shown by the fact that the viscous mass turns into a clear light yellow liquid product. The liquid reaction product catalyst of the present case that is obtained in accordance with the above disclosure is very soluble in many organic solvents and particularly volatile organic solvents such as ethers, acetones, the chlorinated solvents. xylene, toluene, benzene and etc. The solubility indicated that the product was not merely a solution of the organo tin oxide in the hydrocarbon ester since organo tin oxide is highly insoluble in such organic solvents such as the ones specified above. One of the outstanding advantages of the reaction product catalyst of the present case as defined above, is its very high solubility in alkyl silicates and hydrolysis products of alkyl silicates which is the cross-linking agent in two-part RTV systems and also its high solubility in silanol diorganopolysiloxane gums or fluids. Accordingly, one of the outstanding advantages of the reaction product catalyst of the present case which is prepared as specified In addition, nitrogen functional silanes'within the scope of those compounds indicated for formula (1) are those having the formula,

(2) (R ms-.510-

where R is selected from the class consisting of monovalent hydrocarbon radicals and halogenated monova-' lent hydrocarbon radicals of up to IOcarbon atoms, and preferably R is selected from alkyl radicals of l to 5 carbon atoms. In addition, it is preferred that although the a may vary from 0 to 2, that a have a value of 0.

The filler that may be used in the present composition is highly reinforcing filler and semi-reinforcing filler selected from the class consisting of titanium dioxide, litho'pone, zinc oxide, zirconium silicate, silica aerogel, iron oxide, diatomaceous earth, calcium carbonate, fumed silica, precipitated silica, glass fibers, magnesium oxide, chromic oxide, zirconium oxide, aluminum oxide, crushed quartz, calcined clay, asbestos, carbon, graphite, cork, cotton and synthetic fibers. The preferred fillers for the present application are, of course, fumed silica and precipitated silica and particularly fumed silica or precipitated silica that has been treated with various types of siloxane compositions.

The preferred linear fluid organopolysiloxane containing terminal silicon-bonded hydroxy groups and having a viscosity of 500 to 10,000,000 centipoise when measured at 25C, has preferably the formula,

where R? is selected from monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and r is a whole number that varies from 250 to 7,275.

The organosilicate cross-linking agent has the general formula,

where R is a radical selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals, and R is selected from the class consisting of alkyl, haloalkyl, aryl, haloaryl, alkenyl, cycloalkyl, cycloalkenyl, cyanoalkyLalkoxy and acyloxy radicals and it may also comprise a liquid partial hydrolysis product of the aforementioned organosilica'te monomeric compound of formula (4).

The radicals R, R, and R are preferably selected .from the class-consisting of alkyl radicals such as 7 methyl, ethyl, propyl, butyl, hexyl, etc.; aryl radicals such as phenyl, diphenyl, methyl and etc.; alkenyl radicals such as tolyl, xylyl, ethylphenyl and etc.; aralkyl radicals such as benzyl, phenyl, ethyl, and etc.; haloaryl and haloalkyl such as chlorophenyl, tetr'achlorophenyl, difluorophenyl and alkenyl radicals such as vinyl, allyl,

etc. Further, R- may also represent cyanoalkyl, cycloalkyl and cycloalkenyl radicals. The R groups attached to a single silicon radical may be the same groups or different groups. It has been found that at least 50 percent and preferably 70 to 100 percent of the R groups in the diorganopolysiloxane molecule should be methyl. Further, the diorganopolysiloxane can be a homopolymer or a copolymer such as, for example, it has different types of units in the chain such as dimethyl, diphenyl, methyl-phenyl, etc.

The organopolysiloxanes of formula (3) may also be represented by the average unit formula,

m 4ml2 where R is defined above and the value ofm may vary from 1.99 to 2. The average unit formula includes organopolysiloxanes having terminal groups other than hydroxy such as monofunctional and tirfunctional terminal groups. However, in the present case, it is preferred that the terminal groups be hydroxy and the monofunctional and trifunctional groups be kept to a minimum.

Preparation of the diorganopolysiloxanes of formulas (3) and (5) may be carried out by any of the procedures well known to those skilled in the art. Such polysiloxanes can be produced by following a procedure in volving hydrolysis of one or more hydrocarbon substituted dichlorosilanes in which the substituents consist of saturated or unsaturated hydrocarbon groups to produce a crude hydrolyzate containing a mixture oflinear and cyclic polysiloxanes. The crude hydrolyzate is then treated with a suitable catalyst such as KOH so that it can be depolymerized to form a mixture of low boiling, low molecular weight cyclic polymers and undesirable materials such as the monofunctional trifunctional chlorosilane starting material. The resulting composition is fractionally distilled and there is obtained a pure product containing the low boiling, low molecular weight cyclic polymers free of any significant amount of monofunctional and trifunctional groups.

In order to depolymerize the crude hydrolyzate, there is added to said hydrolyzate, KOH and a diphenyl solvent and the mixture is heated at a temperature in the range of 150C to 175C under an absolute pressure of 100 mm of Hg. to produce and remove by evaporation a product consisting of low molecular weight cyclic polysiloxanes comprising, for example, about 85 percent of the tetramer and percent of the mixed trimer and pentamer. Among the cyclic polymers that may so be produced are hexamethylcyclotrisiloxane, octamethylcyclotetrasiloxane and cimethylcyclopentasiloxane. There also may be formed mixtures of cyclopolysiloxanes such as a mixture of octamethylcyclotetrasiloxane and ethylmethylcyclotetrasiloxane, and mixtures of cyclic polymers of dimethylsiloxane with cyclic polymers of diphenylsiloxane, cyclicmethyl- Y, phenylsiloxanes and cyclicmethylvinylsiloxanes.

The pure cyclic polysiloxanes are mixed in the desired proportions to obtain the above defined mixture.

Then the mixture of the cyclic polysiloxanes are subjected to an equilibration procedure to obtain the diorganopolysiloxane of formula (3). The equilibration is preferably carried out at temperatures of about C to C in the presence of a small amount of rearrangement catalyst such as potassium hydroxide, tetrabutyl phosphonium hydroxide, etc. The amount of catalyst used will depend on the extent of the polymerization desired. Generally, 5-10 ppm (parts per million) of the catalyst is sufficient for the polymerization to produce diorganopolysiloxane polymers of a viscosity of 5.0 X 10 to 1.0 X 10 centipoise measured at 25C. There is also present in the reaction mixture 15-150 ppm (parts per million) of water based on the cyclic polymer so as to supply the hydroxy groups which function as chain-stoppers for the linear'diorganopolysiloxane material that is formed. After the equilibration reaction has proceeded for two hours there is reached an equilibration point wherein the mixture contains about 85 percent linear polymers and the amount of linear polymers being formed from the cyclic polymers is equal to the cyclic polymers being formed from the linear polymers.

When this equilibration point has been reached there is added to the mixture a sufficient amount of an acid donor that will neutralize the KOH catalyst so as to terminate the polymerization reaction. Preferably, 1.7 parts per million of tris-(2-chloroethylphosphite) are added to the reaction mixture to liberate HCl which reacts with and neutralizes the KOH and so terminates the equilibration reaction. The cyclicdio-rganosiloxanes in the reaction mixture are then distilled off to leave the polydiorganosiloxane gum which is useful in the present invention. The resulting linear diorganopolysiloxanes are chain-stopped primarily with hydroxy groups and have a viscosity of 5 X 10 to 1.0 X 10 centipoise at 25C. Further, the number of diorgano substituent groups in the siloxane chain is at least 2,150.

High molecular weight diorganopolysiloxanes having a viscosity of 5 X 10 centipoise at 25C and above can be treated with water to arrive at low molecular weight diorganopolysiloxanes having a viscosity of 500 to 5 X 10 centipoise at 25C. This may be accomplished by blowing steam across the surface of the high molecular weight product or through the polymer for a sufficient length of time to obtain the low molecular weight component having the desired silanol content. Thus, it is desirable to obtain the low molecular weight diorganopolysiloxane of formula (4) from a portion of the high molecular weight diorganopolysiloxanes by the above water treatment well known to those skilled in the art so as to reduce the number of diorganosiloxy units from above 7,275 to a value of 250 to 2,150. The use of steam in this fashion will cause a decrease in the viscosity of the polymer while at the same time the formed linear polysiloxane will have terminal siliconbonded hydroxy groups.

Alternatively, the low molecular weight diorganopolysiloxanes can be produced from the high molecular weight diorganopolysiloxane by adding water to them and heating the resulting composition at elevated temperatures of 150C to C so as to break up the long chain polymers into smaller chains. The amount of water used will vary depending upon such factors as the molecular weight of the polymer being treated, the time and the temperature at which the mixture of high molecular. weight diorganopolysiloxanes are heated the low molecular weight organopolysiloxane is produced so that it has a viscosity of 2,000 to 3,000 centipoise at 25C.

In order for the diorganopolysiloxane fluids to cure there must be present in the composition the crosslinking agent of formula (4). In that formula, R groups may be alkyl radicals such as methyl, ethyl, propyl, isopropyl, butyl, amyl, isoamyl, octyl, isooctyl, decyl, dodecyl; haloalkyl such as the chlorinated, brominated, fluorinated alkyl radicals. in addition, R may represent aryl, aralkyl and alkenyl radicals such as vinyl, allyl, phenyl, tolyl, xylyl, benzyl, phenylethyl, naphthyl, anthracyl, biphenyl, as well as the halogen-substituted derivatives of the above radicals. In addition, R represent cycloalkenyl, cycloalkyl and cyanoalkyl radicals. The radical R represents the same radicals as R and, in addition, preferably represents alkoxy and aryloxy radicals such as methoxy, ethoxy, butoxy and phenoxy.

In addition to the monomeric organosilicates of formula (4), there is also preferably used as a cross-linking agent, liquid partially hydrolyzed products of the monomeric silicates. Such hydrolysis products are obtained by effecting partial hydrolysis in water of the particular monomeric organosilicate in the presence of small amounts of acid to a point where it is still waterinsoluble and still possible to isolate a liquid partially hydrolyzed organosilicon compound. Thus, the ethyl silicate having the formula (C H,,O) Si may be partially hydrolyzed by adding acids or acid-forming metal salts to the liquid monomeric organosilicate such as FeCl;,, CuCl AlCl SnCl and thereafter effecting suitable hydrolysis of this mixture of ingredients in water to obtain the two-phase composition from which the water-insoluble, partially hydrolyzed organosilicate can readily be separated from the aqueous phase and catalyst. The partially hydrolyzed ethyl silicate is sold under the tradename Ethyl Silicate-40, by Union Carbide Corporation.

Generally, there is added from 0.1 to 15.0 percent by weight of the cross-linking agent of formula (4) and preferably 0.1 to percent by weight based on the weight of the diorganopolysiloxane of formula (3). If more than 15.0 percent by weight of cross-linking agent is used, the excess does not function as a crosslinking agent since the initial hydroxy positions on the organopolysiloxane .are already reacted with the crosslinking agent and the excess acts as a filler which re,- duces the elasticity of the cured silicone rubber composition. If less than 0.1 percent by weight of cross-linking agent is used, there is not sufficient cross-linking agent to react with the organopolysiloxane to form the cured silicone rubber.

Although the preferable cross-linking agents are organosilicates, there may also be used as cross-linking agents organopolysiloxane resins having a functionality greater than 2 and preferably greater than 2.5. The organopolysiloxane resins are methylsiloxanes, or resins which contain both monomethyl and dimethyl ormon- I ophenyl units. There may also be used ethyls iloxane may resins in which the ratio R"Si is 1.4 to 1 and which mixture contains 15 percent of butoxy groups or there may be used resins in whichthe ratio R"Si is 1.1 to l and which contain 10 percent of methoxy groups or there may be used methylphenylsiloxane resins containing 50 percent of monomethyl units, 25 percent of dimethyl units and 25 percent of monophenyl units.

' Other suitable cross-linking agents are organohydrogenpolysiloxanes of the formula,

in which R is an alkyl or aryl radical and is a number less than 2, but is not zero. The organohydrogenpolysiloxane cross-linking agents have the disadvantage that during curing there is evolved hydrogen gas which can result in bubbles being trapped in the silicone rubber composition. Although the above cross-linking agents can be used in the compositions, the organosilicates of formula l) are preferred since the processability of the composition is facilitated and the cured silicone rubber composition has better physical proper ties. A more detailed description of these other crosslinking' agents is to be found in Nitzsche et al, US. Pat. No. 3,127,363.

There is incorporated into the organopolysiloxane fluid of formulas (3) and (5), a filler which may be of the reinforcing filler type or of the semi-reinforcing type. Generally, the reinforcing fillers have -300 square meter surface areas per gram while thesemireinforcing fillers have a surface area of l-20 square meters per gram.

The reinforcing fillers are added when it is desired to have a high strength silicone rubber composition, that is, a composition with high values for tensile strength and percent elongation. Illustrative of the many fillers which can be employed are titanium dioxide, lithopone, zinc oxide, zirconium silicate, silica aerogel, iron oxide, diatomaceous earth, calcium carbonate, fumed silica, precipitated silica, glass fibers, magnesium oxide, chromium oxide, zirconium oxide, aluminum oxide, crushed quartz, calcined clay, asbestos, carbon,,graph- .ite, cork, cotton and synthetic fibers. There can also be used silica filler treated with an organo cyclic trimer and tetramer such that the tiller is hydrophobic. Generally, there can be added to said diorganopolysiloxane of formulas (3) and/or (5), 5 to 300 percent by weight of filler and preferably 10-200 percent by weight.

Generally, 0.1 to 5 percent by weight of the reaction product of the present case is used based on the weight of the diorganopolysiloxane.

As stated previously, there can be utilized in the twopa rt RTV system of the present case having therein the novel catalyst reaction product, a self-bonding additive of the formulas (1) and (4). It should be understood that these self-bonding additives do not form the basic invention in the present case but are the subject of the copending docket of Warren R. Lampe and Stanley'J. Bessmer, Ser. No. 180,068, filed on Sept. 13, 1971, whose disclosure is hereby incorporated into the present specification by reference. The basic invention in the present case has used the novel reaction product catalyst. of the present case in a two-part'RTV system. lnan alternate and preferred embodiment of the present case, the self-bonding'additives of formulas 1) and (4) may be incorporated into the said two-part RTV wherein R and R are selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and preferably may be selected from the various types of radicals disclosed above for the R radical. Preferably, R and R' are selected from alkyl and aryl radicals of 10 carbon atoms or less and preferably have 1 to 5 carbon atoms. The radicals R R' R, R and R in formula (7) above are selected from the class consisting of hydrogen, alkyl radicals and aryl radicals of up to 10 carbon atoms, M is selected from the class consisting of S and C=O, h is a whole number that varies from 3 to 20 and as pointed out previously a is a whole number that varies from O to 2.

Compounds falling within the-scope of'formula (7) above which are preferred in the present invention for particularly being suited to providing desirable bonding properties for the resulting composition are as follows:

(CHaO)aSiCHzCHzCHz-N O;

(CHaCHzO)aSiCH2CHzCHzN CH2CH2 omonsiomomonm CHzCHa CHzOHz Another class of compounds coming within the scope of formula (4) above have the formula,

(RKDa-Jii-(GH hN(!}H-( 3H-M-R where I? and R are as"previously definedfk is se lected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals, R, R and R are selected from the class consisting of hydrogen, alkyl radicals and aryl rad icals of up to carbon atoms, M is as previously defined. 11 is a whole number that varies from 3 to and a is a whole number that varies from 0 to 2.

Compounds coming within the scope of formula (8) and which are preferred in the; present application are as follows:

. where L is selected from the Another group of nitrogen functional silanes'coming within the scope of formula (4) above have the general formula,

B CH OHC (O CH2CH2)VG where R and R are as previously defined, R and R are selected from the class consisting of hydrogen, alkyl and aryl radicals of up to 10 carbon atoms, B is selected from the classconsisting of nitrogen, sulfur and oxygen, G is selected from the class consisting of atoms,-c'andn are whole numbers that vary from 1 to 10,-D is selected from the class consisting of and oxygen, +is a whole number that varies from 0 to 1, v is a whole number that varies from 1' to 5 and a is a whole number that varies from 0 to 2, as previously stated. I

Preferable compounds in the present case which come within thescope .of formula (9) above are as follows:

omomonsi emu-N Gm-omoH-ii-o-omomN above are of the formula,

(10) 011,61 Rn Ra group consisting of R and RQ-, R and R areas previously'defined, R is selected from the class consisting of alkyl and aryl radicals of up to 10 carbon atoms, R" and R are independently selected from the class consisting of hydrogen, aryl radicals,- alkyl radicals Another class of nitrogen functional silanes which are within the scope of formula (4), are compounds of .the formula,

where R and R are as previously defined, R, R and R are selected from the class'consisting of hydrogen, alkyl radicals and aryl radicals of up to 10 carbon atoms, j is a whole number that varies from 2 to 20, w is a whole number that varies from 1 to 500, A is selected from the class consisting of hydrogen, alkyl radicals, aryl radicals and and a is a whole number that varies from O to 2, as previously disclosed. l

Compounds which are preferred in the present application and which come within the scope of formula (1 1) above, are as follows: a

craca NH Another nitrogenfunctipnal silane coming within the 4 scope of formula (4) above is the nitrogen functional silane ofthc formula,

R1 R, R1! 5 12) won-e l (onlomcms acimmm where R and R are as previously defined, R is selected from the class consisting of hydrogen, alkylradicals and aryl radicals, V is selected from the class consistingof Rand RO, y is a whole number that varies from 0 to 20, .r is a whole number that varies from 2 to 20, and a varies from 0 to 2, as previously stated.

Preferable compounds in the present composition are as follows:

(C1130);Si(CH2)aSl-(CH2)3NH OCH;

OOHa 0H3 (CHaO)sSi(CH2)r-Si-CHz-CH-CHzNHz i OCzHS (CHzO):Si(CH2)r-Si(CHz)aNHg I )C2Hs OCH; (omonsaomnsaoHmNm Another class of nitrogen functional silanes coming within the scope of formula (4) above, are those of the formula,

(R O)aSiOHz-CHCH-C gu Lian J, where R and R are as previously defined, R R R R and R' are independently selected from the class consisting of hydrogen, alkyl radicals, cycloalkyl radicalsand aryl radicals of up to 10 carbon atoms, s is a whole number that varies from 0 to l, u is a whole number that varies from O-to 20, and a is a whole number that varies from 0 to 2. i

The preferred compounds coming within the scope of formula (13) aboveare as follows:

CH3 CH Another class of nitrogen functional silanes coming within the scope of formula (4) above are of the formula,

which come within the scope of formula (12) above,

R andR are defined previously, m is a whole number that varies from 2 to 20 and a is a whole number that'varies from to 2.

Another class of nitrogen functional silanes coming within the scope of formula (2) above, are. nitrogen functional silanes of the formula,

where R and R are as previously defined, R is a radicals elected from. the class consisting of alkyl radicals, cycloalkyl radicals and where two R radicals attached to the same carbon atom taken together with the carbon atom to which they are attached may form a cycloalkyl radical having 5 to 7 carbon atoms, R'- is-a lower alkyl radical such as methyl, ethyl, propyl, i is-a whole v 16 r t Ra es es 304 Ron was.(Ma ada.

where R and R are as defined previously, R, R, R

and R are independently selected from the class consisting of hydrogen, alkyl radicals and aryl radicals of up to 10 carbon atoms, 12 is a whole number that varies from 2 to 10, d is a whole number that varies from 2 to 10 and a is a whole number thatfvaries from O to 2.

Another sub-generic class of nitrogen functional silanes coming within the scopeof formula (4) above are those silanes having the formula,

where R and R are as previously defined, R is independently selected from the classconsisting of hydrogen, alkyl radicals; and aryl radicals of up to 10 carbon atoms, e is a whole-numberthat varies from 1 to l0,f is a whole number that varies from 2 to l0, and a is a whole number that varies from 0 to 2, as previously disnumber that varies from 1 to 4 and a is a whole number 7 a 1' 0: LI L where R and R are as defined previously, R is inde-' pendently selected from the class consisting of hydrogen, lower alkyl radicals, cycloalkyl radicals containing up to 7 carbon atoms, mononuclear and binuclear aryl radicals, mononuclear aryl lower alkyl radicals and fur,- ther radicals whose two R radicals attached to the same carbon atom, taken together with the carbon atoms to which they are attached form a cycloalkyl radical, k is a whole number that varies from 1 to 9 and a is a whole number that varies from 0 to 2.

The above compounds are preferred in the present composition. However, in the case of the compounds of formula 17), as wellas of other compounds coming within the other sub-generic formulas disclosed above, any compound coming within the scope of these formulas can be used as a self-bonding additive that may be added to two-package room temperature vulcanizable silicone rubbercompositions disclosed in the present application, both for the purpose of improving selfbonding properties as well as for the purpose of being used by themselves or in addition with other catalytic agents in the function of acting as catalytic agents.

In addition to the above nitrogen functional silanes there is disclosed by the present case, nitrogen functional silanes coming within the scope of formula (4) above which have the formula,

closed.

Compounds coming within the scope of formula 19) above which are more preferred in the present application are those disclosed above. However, as previously stated any of the compounds disclosed in the subgeneric formula 10) will function in the present application as self-bonding additives as has been discussed previously. I I

As another example ofa sub-generic class of nitrogen functional silanes which come within the scope of formula (4) above and which are preferred in the application of the present case, it is intended to describe and claim in the present application the nitrogen functional silanes of the formula, v

(20) I l, I W R H H R61 H cals, aryl radicals. cycloalkyl radicals containing 5 to 7: carbon atoms, mononuclear and binuclear aryl radicals, mononuclear aryl lower alkyl radicals and further radicals where two R or R radicals attached to the same carbon atom, taken together with the carbon atom to which they are attached form a cycloalkyl radical and in which the different R"" and R radicals may beall the same or different, s is a whole number that varies from I to 4, and a is a whole number that varies from 0 to 2.

In applying the components that are present in the room temperature vulcanizable composition of the present case, the linear diorganopolysiloxane is mixed with filler and color pigments and then stored separately. A second mixture is then composed of the alkyl silicate, with or without a solvent such as xylene the novel reaction product catalyst, and the aminofunctional silane. As a result of the above. there are two mixtures formed -one the base polymer which is stored separately and the other the curing catalyst system which is stored separately. When it is desired to-produce the cured room temperature vulcanizable compo-. sition, the base polymer is mixed with a curing catalyst 3,839,246 Y f 17 1s mixture and-the material is spread, rolled, m'olded or The amino functional silane of formula (4) is preferaf applied in one manner or anotherto the desired applibly used at a concentration of 0.1 to 5 percent and cation. It should be notedthat as these two components more preferably in a concentration of 0.5 to 4 percent are mixed together there is approximately minutes by weight of the linear diorganopolysiloxane. In pracwork time available to mix the two components t 5 tice,it is preferred that one ofthe curing catalysts menth d t ld th lti i t i th d tioned above in the discussion of additional curing cat-. sired surface. Within 20 to 30 minutes after the initial alysts, be used in addition to the amino functional mixture of'the components is carried out at ambient limetemperature the materials have achieved a sufficient There y also he p i the Composition Certain degree of cure (Shore A Hardness to be assumed l0 oxygenated S9]Veht SWh1Ch prolong the Work life of a definite form. After 1 hour, the silicone rubber comthe composmoh Whhout retarding the final cuhe- The position cures to approximately 80 percent of the final use of such solvents may prolong the work life or the Shore A Hardness. After 6 hours very little additional pot life of th composition by at least a factor of 2, but change of Hardness occurs. Preferably,'the mixture of after the silicone rubber composition has been spread the base polymer and the curing agent composition is 15 out to dry the solvents evaporate quickly alllowing the allowed to cure for 24 hours in whatever application it silicone rubber composition to cure rapidly. O xygenis put to so that it develops its full properties at a room ated solvents that may be used are the alcohols, ether temperature vulcanizable silicone composition. The resolvents, ester solvents, ketone solvents and alcohol sulting two-package room temperature vulcanizable ether solvents such as acetone, methanol, isopropanol, silicone rubber composition may be used to form vaributyl ether, ethyl acetate, isoamylketone and methyl ous types of silicone rubber materials. Such a composicell solv tion may also be used to form laminated coatings for The following examples are given for the purpose of various applications such as for coating cloth or for illustrating the invention and are not intended to limit coating roofs. the invention in any way or manner. All parts are by In the case where the room temperature vulcanizable 25 weight.

silicone rubber composition is to be used for coating roofs, then it is desirable to dissolve the base polymer, EXAMPLE i.e., the mixture of the linear diorganopolysiloxane, There is prepared a base polymer solution comprisfiller and coloring agent in one of the common hydroing 100 parts of dimethylpolysiloxane oil which is hycarbon solvents available for that purpose, for example, droxy end-stopped and has a viscosity of 5000 centiinert hydrocarbon solvents such as benzene, toluene, poise at 25C, 160 parts of ground silica filler,'2.0 parts mineral spirits,cyclohexane, xylene and other common of hydrogenated castor oil, 6.4 parts of titanium dioxaliphatic and aromatic solvents. When such a solution ide Color pigments and 1.6 parts of ceramic black. The is formed of the base polymer in the solvent, it is desir above components are mixed together. Then 80 perable to form a solution in which the solvent forms 5 to cent of the above composition is mixed with 20 percent 50 percent by weight of the solution and the base polyby weight of mineral spirits solvent. The above compomer which comprises the linear diorganopolysiloxane, sition forms the base polymer solution.

the filler andthe coloring pigment forms from 50 to 95 The base polymer solution is mixed with the catalytic percent of the solution. This solution of the base polycomposition containing the catalyst which is a reaction mer is then mixed with a curing agent catalyst composiproduct of dibutyl tin oxide and dimethylphthalate, the tion as disclosed above and the solution or mixture of nitrogen functional silane and the ethyl silicate disthe two is then applied or coated on roofs or draperies solved in a solvent. The composition of the catalyst and other type of objects It should be noted that the. mixture is shown in Table 1 below. Further, in Table 1 presence of room temperature vulcanizable silicone below, there is shownthe weight percent of the catalyst rubber composition is especially suited for coating composition used per 100 parts by weight of the polyroofs and that it adheres very strongly and forms a comer solution defined above. The resulting composition hesive bond between the roofing substrate and the siliis cured for the period of time set forth in Table I becone rubber composition. In addition, roofing granules low.

can be applied to the top of the present two-package so The resulting cured two-package room temperature room temperature vulcanizable coating composition vulcanizable silicone composition coating was then and such granules will adhere very strongly to the cured tested for adhesion and the results are indicated in silicone rubber composition of the present case. T ble 1 below.

IhABLE L-SELF-BONDING CHARACTERISTICS OF TWO-PACKAGE COMPOSITIONS 'IO VARIOUS SUBSTRA'IES 'IestNo --1 2 a 4 5 6 7 a 9 Reaction product of dibutyl tin 0.1

oxide and dimethylphthalate.

Reaction product of dibutyl tin 10 10 5 2 0.3 0,1 3.3.

oxide and dimethylmaleate. ylene Mineral spirits 40... 40

Wt. percent of above mixture per 2.0.. 2.0 2.0 2.0 1.2 1.2 1.2

100 parts of base polymer solution. 4 Property:

Cure time, min 30 30 5 5 7 7 60, Tack free tlme,min. 3 18 hrs. 7 hrs 15 l0 15 00 200 20 .2 Final cure (quality) Good Excellent- Excellent- Excellent- Excellent- Excellent- Excellent Excellent.

TABLE I.-SELF-BONDING CHARACTERISTICS OF TWO-PACKAGE COMPOSITIONS T VARIO US SUB ST RATES-Continued Test No 1 2 3 4 5 6 7 s 9 Qualitative adhesion at 24hours:

Plywood Excellent do do do. do do do Excellent Poor. Concrete Good/axe- Marginal Do. Stainless steel d0 Marginal" Good. Excellent .do None. Alelad aluminum. .do MarglnaL Excellent Excellent do do Do. Bare aluminunn D0. Carbon steel (1 Do.

Adhesion-hydrolytic stability at 1 mo.,

120 F., 95+% humidity:

Plywood do Excellent Excellent Excellent Excellent do do do Do. Concrete Good/ext: Marginal Do. Stainless stee do do MarginaL Good do Do. Alelad aluminum Excellent do do Marginal Excellent Excellent do. Do. Bare aluminum" Do. Carbon steel Excellent Do.

In addition, the compositions indicated in Table 1 above, after they are coated on a particular substrate the resulting laminated product is taken and placed in a humidity chamber which was partly filled with water so that the laminated product is partly immersed in water. This humidity chamber is kept at 120F at 95 relative humidity. After one month in this atmosphere the laminated product is taken out and again tested for adhesion. These results are also indicated in Table 1" above.

The above results indicate the excellent self-bonding characteristics of the compositions of the present case, as well as the fact that the bonds that are formed between the silicone rubber composition and the substrate are hydrolytically stable in a far more superior manner than is possible with silicone rubber compositions previously devised. It may also be pointed out that the silicone rubber composition of the present case is self-bonding with superior adhesion to all types of substrates masonry, plastic, metal and wood, including plywood, phenolic, concrete, stainless steel, alclad aluminum, bare aluminum, carbon steel, copper, tin and; other types of such substrates.

EXAMPLE 2 There is prepared a two-part silicone rubber compo sition. The control catalyst is dibutyl tin dilaurate and the reaction product catalyst of the present case is the reaction product of dibutyl tin oxide and dimethylphthalate. The reaction product catalyst as disclosed in' accordance with the above invention is mixed with two General Electric Company RTVs of base componentcompositions which one case was RTV 10.1 and the other case was RTV-10.2 (RTV 10.1 and RTV-10.2

are identification numbers which we use as identifying numbers for the compositions sake of simplicity in these examples. Both are common commercially available components).

The composition of RTV-10.1 comprises 100 parts of a silanol-terrninated dimethylpolysiloxane of 4,000 centipoise at 25C, 25 parts of diatomaceous silica, 65 parts of red iron oxide, and 3 parts of ethyl orthosilicate which is partially hydrolyzed, that is, Ethyl Silicate-40, which is sold by the Union Carbide Corporation. To this RTV-10.1 there is added the indicated amount of catalyst as shown in Table 1 below and the resulting mixture is allowed to cure at room temperature wherein the work life and minutes of the composition ,cated in Table l belowis also mixed in with another RTV composition of-the Silicone Products Department of the General Electric Company, which is known as RTV-I02,

composition of RTV-10.2 comprises parts of a silanol-terminated dimethylpolysiloxane of 3,000:

centipoise viscosity at 25C, 40 parts of calcium carbonate, and 3 parts of the foregoing Ethyl Silicate-40. As indicated in Table 1 below, various amounts of both dibutyl tin dilaurate which functions as the control and also various amounts of the reaction product catalyst of the present case, that is, the reaction product of dibutyl tin oxide and dimethyl phthalate, are mixed into the RTV-10.2 component and the resulting composition is allowed to cure. The work life of the composition in minutes prior to cure is indicated in Table 1 below and the tack-free time of the composition in hours is indicated in Table 1 below.

' T he resuTtin g compositions are also tested in the WPSTM-E-42 Test. (This is a test devised by the Silicone Products Department of the General Electric 'Company to insure deep section cure). This test comprises taking the total composition mixed with the appropriate catalyst as indicated in Table 1 below and the resulting composition is poured into an aluminum dish /8 inch deep and inch in diameter. The dish is then cured at room temperature for 24 hours and the cured rubber is removed from the cup and the Shore A Hardness is determined at the top and bottom of the formed RTV part. This is the measure of the deep section cure. Then the resulting cured product is placed back in the cup and then allowed to cure for 24 hours at room temperature. Then the resulting part after it has been returned to the aluminum cup is taken and placed in an oven at-300F for one hour. It is then cooled to room temperature and again the Shore A Hardness is measured at the top and bottom of the sample. All the compositions set forth in Table 1 below were tested in this E-42 Test, the results of which are indicated in Table 1 below, where A and A are the Shore A Hardness values as measured at the top and bottom of the sample after the cure for 24 hours at room temperature and where the B and B results are the measure of the Shore A Hardness of the sample after it had been 'placed in an oven at 300F for one hour, the sub T" indicating top of the sample and the sub B" indicating the bottom of the sample. The results of this test are set forth in Table 1 below. The results clearly indicate that the samples catalyzed with the catalyst of the present case cured more evenly in deep section cure than the samples that catalyzed with the prior art catalyst, that is, dibutyl tin dilaurate. The results also of the E-42 test set forth in Table 1 below, indicate that the samples which are catalyzedwith the prior art catalyst has less hydrolytic stability and tends to degrade more, that is, Samples A, B and C have a higher hydrolytic stability and a lesser tendency to reversion than the control sample and the D sample which is also a control sample.- The sample compositions are also taken and poured into an aluminum dish /8 inch deep and inch in diameter and after a 24-hour cure at room temperature, the resulting samples are taken and'placed in a pressure cooker which is maintained at lbs. per square inch gauge pressure of stem. The Shore A Hardness of these samples are determined initially before they are inserted in the pressure cooker, after 2 hours in'the pressure cooker, and after 4 hours in the pressure cooker. The resulting Shore A Hardness is indicated in- Table 1 below. The results of these tests indicated that they are catalyzed by the prior art dibutyl tin dilaurate catalyst or catalyzed. by the novel reaction product of the present case, yielded comparable results. The resulting samples are then taken after their physical properties have been determined and placed in an oven for ,24 hours at 480F. After that period of time, the samples are taken out of the oven, cooled at room temperature and the resulting physical properties are once more determined. The results of these physical properties are indicated in Table 1 below. As the results show the samples, that is, the B and C samples, which werev catalyzed with the novel reaction product catalyst of the present case, as compared to the D sample which was catalyzed by the prior art, dibutyl tin dilaurate catalyst, and in which in all samples the amount of tin that was present in the cured composition was the same, the results set forth in Table 1 below indicate that at excessively high temperatures the samples catalyzed with the novel reaction product catalyst of the present case, that is, the B and C samples, retained their physical properties much better and there was less percentage drop in tensile strength in the cured samples than was the case with the D sample. The results are set forth in Table]! below:

TABLE II A Control B C D Component Parts Parts Parts Parts Parts RTV-l0.l I00 I00 I00 RTV-l0.2 I00 100 Solubilized Bu Sn0 (12.9% Sn)" 0.50* 0.50* Solubilized Bu Sn0 (24% Sn)"** 0.25* Bu Sn (Laurate) 0.50" 032* Work Life, minutes 140 180 I20 I45 150 Tack Free Time, hours 3-4 8 16 7-8 7-8 8-9 E-42 Test A 44 48 54 53 51 A 34 v52 5| 44 B, 44 43 49 so 43 B, 35 28 37 38 24 Pressure cooker test (14 psi steam) Shore A Initial 47 50 55 53 54 2 Hours 43 21 -4 Hours 3 34 24 Physical Properties (6" X 6' X 0.080" ASTM slabs) lnitial (I68 hours at room temperature) Shore A 56 56 57 Tensile, psi '757 764 867 Elongation, 3 I I 140 Tear, lbs/in Die B 38 29 35 168 hours at room temperature and 24 hours at 480F Shore A 42 42 44 Tensile, psi 655 688 657 Elongation, 200 200 I90 0.06 wt. Sn on RTV compound tested. 0.09 wt. Sn on RTV compound tested. Reaction product catalyst of dibutyl tin oxide and dimethyl pht the samples catalyzed withthe novel reaction product of the present case are far more hydrolytically stable and have a lesser tendency to reversion than do the samples catalyzed with the prior art dibutyl tin dilaurate catalyst. Of the last three samples, that is, the B,

C and D samples, these compositions are also formed and allowed to cure at room temperature after catalysis with either the dibutyl tin dilaurate or the novel reaction product of the present case. These samples are allowed to cure for 168 hours at room temperature. The samples are then formed into a 6 inch X 6 inch X 8 mils thickness ASTM slab for testing. The resulting samples were then tested for Shore A Hardness, tensile (psi), elongation tear (lbs.)'a'nd Die. B. The results of these tests are set forth in' Table l below. As the results indicate, the resulting cured RTV product whether halate.

and physical properties profile as dibutyl tin dilaurate, ..the prior art catalyst. However, on such tests such as the E42 test which measure the deep section cure .eharacteristics in the A cup and the reversion resistance in the B cup test, the reaction product catalyst of the present case gave improved performance. In a fur- '.ther test, when the samples are exposed to a 15 psi steam environment in a pressure cooker, the Hardness test measurement can be used as an indication of relative hydrolytic stability. From the above data in Table II, it is apparent that the use of the reaction product catalyst of the present case results in less Shore A Durometer drop than the dibutyl tin dilaurate prior art catalyst. It was also decided to run a test in which the shelf-aging characteristics of a two-part RTV system could be measured with both the prior art dibutyl tin dilaurate catalyst and the novel reaction product catalyst of the present case so as to determine the effect of I the catalyst when it is mixed with a cross-linking agent and stored for a substantial period of time.-

orthosilicate sold by Union Carbide Corporation. After. this mixture of catalyst and ethyl orthosilicate were mixed together, Composition E and Composition F were mixed in with the appropriate amount of RTV-' 10.3 which is a commercially available RTV component of a two-part RTV system. RTV 10.3 is an identification number which is used for simplicitypurposes in these examples). In such compositions, there are 1.5 weight percent of Composition Eand Composition F in the total two-part RTV system which are mixed together. The resulting composition is allowed tocure and the cure time in minutes, the tack-free time in minutes and the Shore A Hardness after the composition had been allowed to cure for 24 hours at room temperature is measured. The composition of RTV-10.3 which is indicated in Table III below comprises 100 parts of a silanol-terminated dimethylpolysiloxane of 3,000 centipoise viscosity at 25C, 250 parts of ground silica and parts of iron oxide. The initial cure rate results indicate that the composition having the F component in it, has substantially the same cure time as the composition having Component E and has a much faster tack free time. The Shore A Hardness of both samples are approximately the same.

' Then another test is made by taking Component E and Component F and placing them in an oven at 70C for 4 weeks. At the end of that time, samples of both Component E and Component. F are taken out andmixed with RTV-10.3, that is, sufficient amounts of these shelf aged compositions, Component E and Component F, are mixed in with RTV-10.3 such that in the total composition prepared with each component there is present 1.5 weight percent of Component E and Component F. After this, the composition is allowed to cure and the cure time, tack-free time and Shore A- Hardness after cure at 24 hours at room temperature is determined. The results which are set forth in Table III below indicates that the physical properties ofthe final cured composition changed considerably after Component E has been shelf-aged for 4 weeks at 70C as compared to Component F which has been shelfaged for the same period of time. The results shown.

under the heading Initial Cure" and the results shown under the fAccelerated Shelf Life heading in Table III, indicate that thereis less of a difference when Component F is utilized than is the case when Component E is utilized. The results of these tests are set forth in Table III below:

TABLE III (Control) Component E Parts F Parts Ethyl Silicate-40 30 30 Dihutyl tin dilaurate IO Soluhilized Dihutyl tin oxide reaction product with diethyl phthalatc (247: Sn) l() RTV-10.3 cured with [.5 wtf/i of E & F

PART A Initial Cure Cure Time. minutes 30 25 Tack Free Time. minutes I80 75 Shore A at 24 hours 69 7i PART B Accelerated Shelf Life 4 weeks/70C Cure Time. minutes l0 l3 ;Tack Free Time. minutes 40 70 Shore A at 24 Hours 73 75 The results of Table III above show that in the case when Component F is utilized, that is, the component having the novel reaction product catalyst of the present case, that when this component is utilized in a twopart RTV system there is a smaller change in cure time .as well as in tack free time after the component had been shelf-aged for 4 weeks at 70C, as compared to its cure time and its tack free time before the accelerated shelf aging than was the case with Component E. In the case of Component E as compared to Component F, there is a much more dramatic decrease in cure time and tack free time after Component E has been accelerated, shelf-aged for weeks at 70C, as compared to its cure time and tack-free time immediately-after Component E has been prepared and mixed with RTV-10.3 to form a cured two-part RTV system.

EXAMPLE 3 Component A and Component B, Ethyl Silicate-40 sold by Union Carbide Corporation which is a partially hydrolyzed ethyl orthosilicate. The resulting ingredients are dissolved in mineral spirits solvent in which the self- :bonding additive, the Ethyll Silicate-40 and the catalyst are soluble in. The composition of Component A and Component B of a two-part RTV system are set forth in Table IV below. i

TABLE iv Parts y-aminopropyltriethoxysilane 25 22.5 Ethyl Silicate-40 12.5 I 1.25 Dihutyl tin dilaurate 12.5 Reaction product catalyst of dihutyl tin oxide and diethyl malente (25% Sn) 3.75 Mineral Spirits 50 62.5

Both of these components are mixed into Silicone Products Department, General Electric Company's 25 RTV-10.4. which is a commercially available component for a two-part RTV system. (RTV-10.4 is an identitication number that is used solely in this application).

The composition of RTV-10.4 comprises 27 percent by; weight of the total composition of silanol-terminated dimcthylpolysiloxane at 8,000 centipoise viscosity at 25C, 41 percent by weight of ground quartz, 12 percent by weight of red color masterbatch and 20percent by weight of solvent which in this case is mineral spirits. To two different samples-of RTV-10.4, there are added in one case 12.0 weight percent of Component A based on the weight of the total composition and 8.0 weight percent of Component B based on the weight of the total composition. The resulting compositions are then applied to plywood and Alclad aluminum panels in a film thickness comprising 20 mils thick and allowed to cure at room temperature. Cure rate tests were run on the catalyzed samples and the results are presented in Table V below.

TABLE v Component A B Cure Time, minutes 3 3 Tack Free Time. minutes 5 Firm Cure Time, minutes 30 60 The results of this table show that the Component B utilizing the novel catalyst reaction product of the present case has a comparable cure rate to the composition having Component A in there with the prior art dibutyl tin dilaurate catalyst. After the RTV compositions having both Component A and Component B are placed on plywood and allowed to cure for about an hour, the

samples are tested for adhesion and the results are indicated in Table VI below. The samples on the Alclad aluminum are allowed to cure for 24 hours at room temperature and then the adhesion in both samples,

that is, the sampleshaving Component A and Component B, are tested for adhesion and the results are indicated in Table VI below. After that time, the panels are then placed in a humidity chamber maintained at 95 percent Relative Humidity at a temperature of 120F and the samples remained in the chamber for a period of three weeks after which period the samples were taken out of the humidity chamber, allowed to cool to room temperature and tested for adhesion. The results of these tests are set forth in Table VI below.

TABLE VI Composition Adhesion to plywood after one hour Marginal Excellent Adhesion to Alclad aluminum at 24 hours Fair-Good Excellent Sample Change after 4 weeks/l F/95+7r RH Discolored. Very slight surface chalked and discoloration. No

embrittled loss of adhesion with loss of coating still has adhesion flexibility The results in Table VI indicate that the compositions catalyzed with the novel reaction product catalyst of the present case had much better self-bonding prop.-

erties and better hydrolytic resistance than the compo-" sitions which were catalyzed with Component A which contained the prior art,'dibutyl tin dilaurate.

LII

' .number that varies from 0 to 2.

where R is a radical selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and R is selected from the class consisting of alkyl, haloalkyl, aryl, haloaryl, alkenyl, cycloalkyl, cycloalkenyl, cyanoalkyl, alkoxy and acyloxy radicals and (2) a liquid partial hydrolysis product of the aforementioned organosilicate monomeric compounds. 7

d. from 0.1 to 5 percent by weight of the organopolysiloxane of a catalyst which is the reaction product of an organo tin oxide having the formula RIIRIIISnO where R and R are monovalent hydrocarbon radicals with a hydrocarbon ester selected from the class consisting of esters of monocarboxylic acids, esters of ,dicarboxylicacids and esters of inorganic acids containing at least one oxygen atom in the said radical attached to a replaceable hydrogen atom, and where .:there is reacted from 6 to 1 moles of the organo tin xid Petmctepf eesteuv eatheteactiquissa out ata temperature in the range from room temperature to 250C.

2. The composition of claim 1 wherein in said catalyst R" and R are selected from alkyl and aryl radicals of up to 18 carbon atoms.

3. The composition of claim 2 wherein in said catalyst said hydrocarbon ester is of the inorganic acid.

4. The composition of claim 2 wherein in said catalyst said hydrocarbon ester is of the monocarboxylic acid or the dicarboxylic acid.

5. The composition of claim 1 which is self-bonding by having therein 0.1 to 1.0 percent by weight of a nitrogen-functional .silane of the formula,

R is selected from the classconsisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals, Z is a hydrolyzable group selected from the class consisting of alkoxy, phenoxy, and dialkylamino, 0 is a nitrogen functional radical which may contain in addition to the nitrogen functionality a saturated, unsaturated or aromatic hydrocarbon residue functionalized by a member selected from the class consisting of amino, cyano, 0x0 and ester, a is a whole 6. Thecomposition of claim 5 wherein the nitrogenfunctional silane is. of the formula,

$l a on sio,

where R is selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals of up to'l0 carbon atoms.

7. The composition of claim 5 wherein the organo-.

. polysiloxane of (a) is a diorganopolysiloxane which has the formula,

9. The composition of claim 5 wherein said catalyst is used at a concentration of 0.1 to 3.0 percent by' weight of the organopolysiloxane.

'10. The composition of claim 1 wherein there is utilized 5 to 300 percent by weight of filler based on.the weight of the organopolysiloxane.

11. The composition of claim wherein the filler is highly reinforcing filler and semi-reinforcing filler se-= lected from the class consisting of titanium dioxide, lithopone, zinc oxide, zirconium silicate, silica aerogel, iron oxide, diatomaceous earth, calcium carbonate, fumed silica, precipitated silica, glass fibers, magnesium oxide, chromic oxide, zirconium oxide, aluminum oxide, crushed quartz, calcined clay, asbestos, carbon, graphite, cork, cotton and synthetic fibers.

12. The composition of claim 1 which further includes therein a low molecular weight organopolysiloxane fluid which is composed of (R* SiO units, (R );,SiO,, units and R SiO units having 0.05 percent to 8 percent by weight of hydroxy radicals, where the ratio of the organosiloxy units to the diorganosiloxy units is from 0.1 l to 1.4, inclusive, and the ratio of the triorganosiloxy units to diorganosiloxy units is from 0.02 to about 1, such that said fluid may be linear or branched chain where R is an alkyl radical.

13. The composition of claim 5 wherein the nitrogenfunctional silane is present at a concentration of 0.1 to 5 percent by weight of the linear organopolysiloxane having terminal silanol groups thereon.

14. The composition of claim 5 wherein the nitrogenfunctional silane has the formula,

Rn m

I Rn R" (EH-0 H I l l )3"l CH hN /M,

CHI-CH I 60 wherein R and R are selected from the class consisting of monovalent hydrocarbon radicalls andhalogenated monovalent hydrocarbon radicals, R, R h R, R and R are selected from the class consisting of hydrogen, alkyl radicals andv aryl radicals of up to 10 carbon atoms, M isselected from the class consisting of S0 and C=O, h is a whole number that varies from 3 to 20, and a is a whole number that varies from 0 to 2.

15. The composition of claim 14 wherein the silane has the formula,

CHz-CE:

n H I 16. The composition of claim 5 wherein the nitrogenfunctional silane has the formula,

where R, R and R are selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals and R', R

20 and R are selected from the class consisting of hydrogen, alkyl radicals and aryl radicals of up to [0 carbon atoms, M is selected from the class consisting of S0 and C=0, I1 is a whole number that varies from 3 to 20, and a is a whole-number that varies from 0 to 2.

17. The composition ofclaim 5, wherein the nitrogen-functional containing silane has the formula,

35 lected from the class consisting of hydrogen, alkyl and 'aryl radicals of up to 10 carbon atoms, B is selected from the class consisting of nitrogen, sulfur and oxygen, G is selected from the class consisting of N and Now:

. W... c a, l 'where R is selected from the class consisting of hydrogen, alkyl radicals and aryl radicals of up to 10 carbon latoms, c and n are whole numbers that vary from 1 to l0, D is selected from theclass consisting of and oxygen, is a whole number that varies from O to l, v is a whole number that varies from 1 to 5 and a is a while number that varies from O to 2.

18. The composition of claim 17 wherein the nitrogen-functional silane has the formula,

l9. Thecomposition of claim 5 wherein the nitrogenfunctional silane has the formula,

R, g 0 R; R;

lwmtataatatml where L is selected from the group consisting of R N- and RO, R and R are selected from the class consisting of monovalent hydrocarbon radicals and monovalent halogenated hydrocarbon radicals, R is selected from the class consisting of alkyl and aryl radicals of up to 10 carbon atoms, R and R are independently selected from the class consisting of hydrogen, aryl radicals, alkyl radicals,

R"CN and --R"OR, where R is a divalent hy' drocarbon radical selected from the class consisting of alkenylene and arylene radicals of up to 10 carbon atoms, n is a whole number that varies from 1 to 20 and a is a whole number that varies from to 2.

lected from the class consisting of hydrogen, alkyl radicals and aryl radicals of up to 10 carbon atoms, j is a wholenumber that varies from 2 to 20, w is a whole number that varies from 1 to 500, A is selected from the class consisting of hydrogen, alkyl radicals, aryl. 5

radicals and and a is a whole number that varies from 0 to 2.

22. The composition of claim 21 wherein the nitrogen-functional silane is of the formula,

30 number that varies from 0 to 20, x is a whole number that varies from 2 to and a varies from 0 to 2.

24. The composition of claim 23 wherein the nitrogen-functional silane has the formula,

OCH;

(CHaO): Si(GHz) rSi-(CH2)aN 2- OCH:

- The composition of claim 5 wherein the nitrogenfunctional silane is of the formula,

out J.

where R and R are selected from the class consisting. of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals, R R R R and 2O R" are independently selected from the class consisting of hydrogen, alkyl radicals, cycloalkyl radicals and aryl radicals of up to 10 carbon atoms, 5 is a whole number that varies from 0 to l, u is a whole number that varies from O to 20 and a is a whole number that varies from O to 2.

26. The composition of claim 25 wherein the nitrogen-functional silane is of the formula,

27. The composition of claim 5 wherein the nitrogenfunctional silane is of the formula,

where and R are selected the class consisting of mews elem.MQcarbeara n.d..habg

lmonovalent hydrocarbon radicals, R and R are independently selected from hydrogen, alkyl radicals gand aryl radicals of up to 10 carbon atoms, z is a lwhole number that varies from 2 to 20 and a is a whole-number that yaries from 0 to 2 28. The composition of claim 27 wherein the nitrogen-functional silane has the formula,

CgHg

(CHzOhSlCHgCHaCHzN CgHs (CH O) SiCH CH CH SCH CH NHCH CH NH 29. Thecomposition of claim 5 wherein the nitrogen- 23. The composition of claim 5 wherein the nitrogenfunctional silane is of the formula,

R]. R.(R" O (R ohudl where R and R are selected from monovalent hydrocarbon radicals and monovalent halogenated hydrocar- 5 bon radicals, R is selected from the class consisting of hydrogen, alkyl radicals and aryl radicals, V is selected from the class consisting of and RO--, y is a whole 7 functional silane has the formula,

R. (R OhqdKGHimNHz,

cu cu onsica cu cumu 31. The composition ofclaim 5 wherein the nitrogenfunctional silane is of the formula,

where R and R are selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals, R" is a radical selected from the class consisting of alkyl radicals, cycloalkyl radicals and where two R radicals attached to the same carbon atom, taken together with the carbon atom to which they are attached, may form a cycloalkyl radical having 5 to 7 carbon atoms, R is a lower alkyl radical, i is a whole number that varies from I to 4 and a is a whole number that varies from to 2.

32. The composition of claim 31 wherein the nitrogen-functional silane has the formula.

33. The composition of claim wherein the nitrogenfunctional silane is of the formula,

carbon atom, taken together with the carbon atoms to which they are attached, form a cycloalkyl radical, k is a whole number that varies from 1 to 9 and a is a whole number that varies from O to 2.

34. The composition of claim 33 wherein the nitrogen-functional silane is of the formula,.

(CH ,O );;SiCH=CH-C(CH;, O-CH. ,CH CH- ,NH-

35. The composition of claim 5 wherein the nitrogenfunctional silane is of the formula,

R,I R03 R05 R04 R05 (t I (t I )3-.s1 H N-H 1r N-H,

where R and R are selected from the class consisting of monovalent hydrocarbon radicals, R'', R, R and R are independently selected from the class consisting of hydrogen, alkyl radicals and aryl radicals of up to H) carbon atoms. I) is a whole number that varies from 2 to l0, :1 is a whole number that varies from Z to l() and a is a whole number that varies from O to 2.

36. The composition ofclaim 5 wherein the nitrogenfunctional silane has the formula.

1'}, 1 1]}, l ]]{tt 0 -C-NII, Avil 'm where R and R are selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals, R is independently selected from the class consisting of hydrogen, alkyl radicals and aryl radicals of up to 10 carbon atoms. 0 is a whole number that varies from 1 to l0,f is a whole number that varies from 2 to l() and a is a whole number that varies from 0 to 2.

37. The composition of claim 36 wherein the nitrogen-functional silane has the formula,

38. The composition of claim 5 wherein the nitrogenfunctional silane has the formula.

where R and R are selected frommonovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals, R and R are independently selected from hydrogen, alkyl radicals, aryl radicals, cycloalkyl radicals containing 5 to 7 carbon atoms, mononuclcar and binuclear aryl radicals, mononuclcar aryl lower alkyl radicals and further radicals where two R or R radicals attachcd to the same carbon atom, taken together with the carbon atoms to which they are attached, form a cycloalkyl radical and in which the diffe'rent R' and R radicals may be allthe same or different, .s' is a whole number that varies from l to 4, and a is a whole number that varies from O to 2.

39. The composition of claim 38 wherein the nitrogen-functional silane is of the formula,

heptane and octane. 

1. A TWO-PART ROOM TEMPERATURE VULCANIZABLE SILICONE RUBBER COMPOSITION WITH IMPROVED HYDROLYTIC RESISTANCE COMPRISING, A. A LINEAR, FLUID ORGANOPOLYSILOXANE CONTAINING TERMINAL SILICON-BONDED HYDROXY GROUPS AND HAVING A VISCOSITY OF 500 TO 10,000.000 CENTIPOISE WHEN MEASURED AT 25*C, THE ORGANIC GROUPS OF THE AFORESAID ORGANOPOLYSILOXANE REPRESENTING MONOVALENT HYDROCARBON RADICALS, B. A FILLER, C. FROM 0.1 - 15 PERCENT BY WEIGHT OF AN ALKYL SILICATE SELECTED FROM THE CLASS CONSISTING OF (1) A MONOMERIC ORGANOSILICATE CORRESPONDING TO THE GENERAL FORMULA,
 2. The composition of claim 1 wherein in said catalyst R'''' and R'''''' are selected from alkyl and aryl radicals of up to 18 carbon atoms.
 3. The composition of claim 2 wherein in said catalyst said hydrocarbon ester is of the inorganic acid.
 4. The composition of claim 2 wherein in said catalyst said hydrocarbon ester is of the monocarboxylic acid or the dicarboxylic acid.
 5. The composition of claim 1 which is self-bonding by having therein 0.1 to 10 percent by weight of a nitrogen-functional silane of the formula,
 6. The composition of claim 5 wherein the nitrogen-functional silane is of the formula,
 7. The composition of claim 5 wherein the organopolysiloxane of (a) is a diorganopolysiloxane which has the formula,
 8. The composition of claim 1 wherein the alkyl silicate is polyethyl silicate and is present in an amount of 0.1 to 10 percent by weight of the organopolysiloxane.
 9. The composition of claim 5 wherein said catalyst is used at a concentration of 0.1 to 3.0 percent by weight of the organopolysiloxane.
 10. The composition of claim 1 wherein there is utilized 5 to 300 percent by weight of filler based on the weight of the organopolysiloxane.
 11. The composition of claim 10 wherein the filler is highly reinforcing filler and semi-reinforcing filler selected from the class consisting of titanium dioxide, lithopone, zinc oxide, zirconium silicate, silica aerogel, iron oxide, diatomaceous earth, calcium carbonate, fumed silica, precipitated silica, glass fibers, magnesium oxide, chromic oxide, zirconium oxide, aluminum oxide, crushed quartz, calcined clay, asbestos, carbon, graphite, cork, cotton and synthetic fibers.
 12. The composition of claim 1 which further includes therein a low molecular weight organopolysiloxane fluid which is composed of (R42)2SiO units, (R42)3SiO1/2 units and R42SiO3/2 units having 0.05 percent to 8 percent by weight of hydroxy radicals, where the ratio of the organosiloxy units to the diorganosiloxy units is from 0.11 to 1.4, inclusive, and the ratio of the triorganosiloxy units to diorganosiloxy units is from 0.02 to about 1, such that said fluid may be linear or branched chain where R42 is an alkyl radical.
 13. The composition of claim 5 wherein the nitrogen-functional silane is present at a concentration of 0.1 to 5 percent by weight of the linear organopolysiloxane having terminal silanol groups thereon.
 14. The composition of claim 5 wherein the nitrogen-functional silane has the formula,
 15. The composition of claim 14 wherein the silane has the formula,
 16. The composition of claim 5 wherein the nitrogen-functional silane has the formula,
 17. The composition of claim 5, wherein the nitrogen-functional containing silane has the formula,
 18. The composition of claim 17 wherein the nitrogen-functional silane has the formula,
 19. The composition of claim 5 wherein the nitrogen-functional silane has the formula,
 20. The composition of claim 19 wherein the nitrogen-functional silane is of the formula,
 21. The composition of claim 5 wherein the nitrogen-functional silane has the formula,
 22. The composition of claim 21 wherein the nitrogen-functional silane is of the formula, (CH3O)3SiCH2CH2CH2SCH2CH2NHCH2CH2NH2.
 23. The composition of claim 5 wherein the nitrogen-functional silane is of the formula,
 24. The composition of claim 23 wherein the nitrogen-functional silane has the formula,
 25. The composition of claim 5 wherein the nitrogen-functional silane is of the formula,
 26. The composition of claim 25 wherein the nitrogen-functional silane is of the formula,
 27. The composition of claim 5 wherein the nitrogen-functional silane is of the formula,
 28. The composition of claim 27 wherein the nitrogen-functional silane has the formula,
 29. The composition of claim 5 wherein the nitrogen-functional silane has the formula,
 30. The composition of claim 29 wherein the nitrogen-functional silane is of the formula, (CH3CH2O)3SiCH2CH2CH2NH2.
 31. The composition of claim 5 wherein the nitrogen-functional silane is of the formula,
 32. The composition of claim 31 wherein the nitrogen-functional silane has the formula, (CH3O)3SiCH2CH2CH2OCH2-CH-CH2NH2.
 33. The composition of claim 5 wherein the nitrogen-functional silane is of the formula,
 34. The composition of claim 33 wherein the nitrogen-functional silane is of the formula, (CH3O)3SiCH CH-C(CH3)2O-CH2CH2CH2NH2.
 35. The composition of claim 5 wherein the nitrogen-functional silane is of the formula,
 36. The composition of claim 5 wherein the nitrogen-functional silane has the formula,
 37. The composition of claim 36 wherein the nitrogen-functional silane has the formula, (CH3O)3SiCH2CH2CH2-S-CH2CH2NH2.
 38. The composition of claim 5 wherein the nitrogen-functional silane has the formula,
 39. The composition of claim 38 wherein the nitrogen-functional silane is of the formula, (CH3O)3SiCH CH-C(CH3)2OCH2CH2CH2CH2NHCH2CH2CH2NH2.
 40. The silicone rubber composition of claim 1 wherein there is further present 5 to 50 percent by weight of the total composition of an aromatic or aliphatic solvent selected from the group consisting of xylene, cyclohexane, toluene, mineral spirits, benzene, heptane and octane. 